Item # 02Y037, 02Y037 Epoxy Primer on AST ACME, Inc.

AST Acme, Inc. - High Performance Coatings & Sheet Linings

		Call Us: 502-583-8355 \| Email: info

Fluoropolymer Coatings

Rubber & Tank Linings

Press Releases

Learn more About
AST Acme, Inc.
-Typical Application
-Tank Linings
-Service Package
-Safety
-Capabilities
-Experience

All Categories > Military Coatings > Concrete Saver® Anti-Slip Floor Coatings Heavy Vehicle Grade AS9100 System > MIL-PRF-23377D, E & F Type I Class 1 Epoxy Primer > Item # 02Y037

Printable Page Email

Email This Page

Save To Favorites


	Item # 02Y037 02Y037 Epoxy Primer

Email This Page

Save To Favorites

larger image

02Y037 is designed for conventional and electrostatic spray application.
The 02Y037 is chemically cured, two-component, conventional solids, epoxy-polyamide primers for application on aircraft and aerospace equipment. Component A contains the pigment and epoxy resin. Component B is a clear, non-pigmented polyamide component, which acts as a hardener or curing agent for Component A. When these epoxy primers are used over properly prepared substrates, they provide a corrosion inhibiting, chemical and solvent resistant film suitable for topcoat. The cured primers are resistant to immersion in water, jet fuels, lubricating oils and hydraulic fluids.

Specifications · Typical Characteristics (Before Reduction)

Specifications

Application		Conventional and Electrostatic Spray

Shelf Life		1 year when stored between 35 - 115°F in original, unopened containers away from direct sunlight.

Dry Times @ 63 - 85°F, 0.6- 0.9 mils		Dry hard : 6 hours max Dry to topcoat : 5 hours max May be forced dried for "dry to stack" conditions. Tack free : 1 hour max

Typical Characteristics (Before Reduction)

Color¹

Yellow

Mix Ratio, by Volume

1 parts base to 1 part catalyst

Reducer

IS-237

Induction Time

No induction necessary

Recommended Dry Film Thickness

0.6 - 0.9 mil

Initial Mixed Viscosity

40 seconds max, #4 Ford

Average Theoretical Weight Mixed

8.8 ± 0.2 lb/gal

Average Theoretical % Solids By Weight, Mixed

44.3% ± 0.5

Average Theoretical % Solids By Volume, Mixed

29.0% ± 0.7

Average Theoretical Coverage @ 1 mil Dry Film Thickness

464-sq.ft ± 12 @ 100% transfer efficiency

Pot Life @ 63 - 85°F

8 h

Max. Coatings VOC

600 g/L
5.0 lb/gal

¹ Characteristics are calculated based on product formula and raw material characteristics reported by raw material suppliers. Values are thought to be representative, but they are not to be treated as specifications.